Abstract
A telechelic organic–inorganic polymer (SiPPSU) where –SiPh(OH)2 groups are covalently linked to the polymeric chain of polyphenylsulfone (PPSU) was prepared and characterized. The polymer was sulfonated up to a degree of sulfonation (DS) equal to 2 (SiSPPSU), then used to prepare blends with sulfonated polyetheretherketone (SPEEK) having DS = 0.9 in 5 and 10 wt.% concentration. The synthesized polymers and the blends were characterized by ATR/FT-IR spectroscopy. Membranes were prepared with these materials and their proton conductivity was measured using electrochemical impedance spectroscopy (EIS). The formation of the blends substantially altered the physicochemical characteristics of SPEEK: the membrane prepared with the blend at the concentration of 5 wt.% exhibited high and stable conductivity values at 120 °C: both when dry (σ = 6.1 × 10−3 S/cm) and wet conditions (σ = 6.4 × 10−2 S/cm for a 50% water uptake), hence, being suitable for application as electrolyte in intermediate temperature polymer electrolyte membrane fuel cells (PEMFCs)
Details
Published on: Journal of Membrane Science 2006, 279, 186-191
Authors: M. L. Di Vona, A. D’Epifanio, D. Marani, M. Trombetta, E. Traversa, S. Licoccia