Abstract
Mixed membrane matrices (MMMs) made up with Nafion and nanocrystals of zirconium metal–organic framework (MOF) UiO-66 or the analogous sulfonated SO3H-UiO-66 were prepared by varying the filler loading and the size of the crystals. The combined effects of size and loading, together with the presence of sulfonic groups covalently linked to the MOFs, were studied with regard to the conductivity and mechanical properties of the obtained composite matrices. A large screening of membranes was preliminarily made and, on the most promising samples, an accurate conductivity study at different relative humidities and temperatures was also carried out. The results showed that membranes containing large crystals (200 nm average size) in low amounts (around 2%) displayed the best results in terms of proton conductivity values, reaching values by 30% higher than those of pure Nafion, while leaving the mechanical properties substantially unchanged. On the contrary, MMMs containing MOFs of small size (20 nm average size) did not show any conductivity improvements if compared to pure Nafion membranes. The effect of MOF sulfonation was negligible at low filler loading whereas it became important at loading values around 10%. Finally, membranes with a high filler loading (up to 60 wt %) of sulfonated UiO-66 showed a slight reduction of conductivity in comparison with membranes loaded at 20% of nonsulfonated ones.
Illustrations
Details
Published on: ACS Applied Materials & Interfaces 2017, 9, 42239-42246
Authors: A. Donnadio, R. Narducci, M. Casciola, F. Marmottini, R. D’Amato, M. Jazestani, H. Chiniforoshan, F. Costantino